Japan Atomic Energy Agency
Thermodynamic database for nuclear fuels and
reactor materials

Thermodynamic data

ZrO2 (mon)

Temperature (T)
[K]
Specific heat capacity (Cp)
[J/molK]
Enthalpy (H)
[J/mol]
Entropy (S)
[J/molK]
Gibbs energy (G)
[J/mol]
298.1500063.43494-1.10097E650.72468-1.11609E6
300.0000063.46852-1.10085E651.11718-1.11619E6
400.0000065.42172-1.09441E669.63886-1.12226E6
500.0000067.43415-1.08777E684.45410-1.12999E6
600.0000069.37357-1.08092E696.92179-1.13908E6
700.0000071.19468-1.07389E6107.75421-1.14932E6
800.0000072.87855-1.06669E6117.37245-1.16059E6
900.0000074.41613-1.05932E6126.04654-1.17277E6
1000.0000075.80267-1.05181E6133.96016-1.18577E6
1100.0000077.09307-1.04417E6141.23789-1.19953E6
1200.0000078.33631-1.03640E6147.99946-1.21399E6
1300.0000079.54508-1.02850E6154.31764-1.22911E6
1400.0000080.72843-1.02049E6160.25600-1.24485E6
1500.0000081.89249-1.01236E6165.86548-1.26115E6
1600.0000083.04153-1.00411E6171.18745-1.27801E6
1700.0000084.17860-9.95748E5176.25598-1.29538E6
1800.0000085.30594-9.87274E5181.09945-1.31325E6
1900.0000086.42522-9.78687E5185.74173-1.33160E6
2000.0000087.53767-9.69989E5190.20308-1.35040E6
2100.0000088.64428-9.61180E5194.50085-1.36963E6
2200.0000088.93468-9.52290E5198.63639-1.38929E6
2300.0000088.99157-9.43394E5202.59067-1.40935E6
2400.0000089.10674-9.34490E5206.38040-1.42980E6
2500.0000089.25561-9.25572E5210.02084-1.45062E6
2600.0000089.42400-9.16638E5213.52475-1.47180E6
2700.0000089.60359-9.07687E5216.90298-1.49332E6
2800.0000089.78938-8.98717E5220.16500-1.51518E6
2900.0000089.97833-8.89729E5223.31911-1.53735E6
3000.0000090.16858-8.80721E5226.37272-1.55984E6